Supplier of Graphite Electrode Scrap

• Type: Graphite Electrodes
• Composition: C
• Carbon Content: High-Carbon
• Grade: RP
• Forming Way: Extruded Graphite
• Crystal Morphology: Graphiting
• Model NO.: RP/HP/UHP
• Size: 200-600mm
• Resistivity: 4.6-5.8
• Application: Eaf and Lf Furnace for Steel Melting
• Bulk Density: 1.68-1.74 g/cm3
• Modulus of Rupture: 10-14 MPa
• Delivery Time: 7 Days (Within 100tons)
• Transport Package: Wooden Cases
• Specification: RP/HP/UHP
• Trademark: YJ
• Origin: Shandong Dezhou
• HS Code: 85451100
• Production Capacity: 25000mt

Product Description

Linyi Yanjun Carbon Material Co., Ltd. is located at No. 26 Huaxing Road, Hengyuan Economic Development Zone, Linyi County, Dezhou City, Shandong Province. Our company covers an area of 100,000 square meters which has passed ISO9001:2015 quality management system certification, ISO45001:2018 occupational health and safety management system certification and ISO14001:2015 environment management system certification.
Our company mainly produces regular power, high power and ultra-high power Graphite Electrode with a diameter of Φ150mm-Φ600mm, Graphite Plates and Graphite Columns (mainly used in graphitization furnaces to graphite lithium ion battery cathode material), Graphite Blocks with various sizes, and different sizes and grades of Carbon Raiser.
Our company has a complete production line of calcining, crushing, sieving, batching, mixing-kneading, forming, baking, impregnation, graphitization, lathing and sawing machines processing, with advanced technology level, complete testing and inspection process, high-level technical personnel and perfect after-sales service.
Linyi Yanjun Carbon Material Co., Ltd. sincerely welcomes customers and cooperators to visit and achieve mutual benefit development.


Specifications for RP, HP, UHP graphite electrodes with nipples:

RP	HP	UHP
Electrode: Bulk Density≥ 1.56g/cm3  Specific Resistivity≤ 8.5μm  Bending Strength≥ 10.0MPa  Elastic Modulus≤ 9.3GPa Thermal Expansion Coefficient≤ 2.7x10 -6/°C Ash≤ 0.5%   Nipple: Bulk Density≥ 1.68g/cm3  Specific Resistivity≤ 7.0μm  Bending Strength≥ 14.0MPa Elastic Modulus≤ 13.7GPa Thermal Expansion Coefficient≤ 2.5 x10 -6/°C Ash≤ 0.5%	Electrode: Bulk Density≥ 1.65g/cm3  Specific Resistivity≤ 6.5μm  Bending Strength≥ 12.0MPa  Elastic Modulus≤ 10.0GPa Thermal Expansion Coefficient≤ 2.2x10 -6/°C Ash≤ 0.3%   Nipple: Bulk Density≥ 1.74g/cm3  Specific Resistivity≤ 5.5μm  Bending Strength≥ 16.0MPa Elastic Modulus≤ 14.0GPa Thermal Expansion Coefficient≤ 2.0 x10 -6/°C Ash≤ 0.3%	Electrode: Bulk Density≥ 1.68g/cm3  Specific Resistivity≤ 5.8μm  Bending Strength≥ 16.0MPa  Elastic Modulus≤ 14.0GPa Thermal Expansion Coefficient≤ 1.9x10 -6/°C Ash≤ 0.2%   Nipple: Bulk Density≥ 1.76g/cm3  Specific Resistivity≤ 4.5μm  Bending Strength≥ 18.0MPa Elastic Modulus≤ 16.0GPa Thermal Expansion Coefficient≤ 1.4 x10 -6/°C Ash≤ 0.2%